PEROXAN DC-P +
Dialkyl peroxide / Polymerization / Curing / Crosslinking
Dicumyl peroxide
98%,
Powder
PEROXAN DC-P+ is used for the curing of unsaturated polyester resins.
TDS UP
PEROXAN DC-P+ is used for the crosslinking of natural rubber and synthetic rubber, as well as polyolefins.
TDS CL
« back
PEROXAN DC-P +
Molecular weight:
CAS No.:
270.4
80-43-3
Appearance:
Peroxide assay:
Active oxygen assay:
Bulk density at 20°C:
white powder
min. 98%
min. 5.8%
400 kg/m³
in an EPDM compound:
Maximum storage temperature (Ts max):
Storage stability as from date of delivery:
30°C
6 months
Keep packaging tightly closed in a well ventilated place at indicated storage temperature. Keep away from reducing agents e.g. amines, acids, alkalis, heavy metal compounds (e.g. accelerators, driers, metal soaps). Never weigh out in storage room.
Oxidizing agent. Decomposes violently under the influence of heat or by contact with reducing agent. Never mix with accelerators.
Organic Peroxides are more or less stable products but will decompose under the influence of heat. To minimize a loss of quality during storage, it is important that the recommended maximum storage temperature is not exceeded. If a minimum storage temperature is given, an undesirable process such as a solidification or phase separation, is known to occur below this temperature.
|
Flash point: SADT: |
>SADT°C 80°C |
|
|
The SADT (Self Accelerating Decomposition Temperature) is the lowest temperature at which a self accelerating decomposition may occur.
|
Schlavenhorst 71 D-46395 Bocholt Germany |
Phone: +49 (0)2871 / 99 02-0 Fax: +49 (0)2871 / 99 02-50 www.pergan.com |
HPUPCL/003/1019 Page 1 of 2 |
PEROXAN DC-P +
Dialkyl peroxide / Polymerization / Curing / Crosslinking
PEROXAN DC-P+ is used for the curing of unsaturated polyester resins at elevated temperatures.
PEROXAN DC-P+ is preferred for the curing of UP resin based hot press moulding formulations in the temperature range from 130° to 170°C. It is specially suitable for GMC; as a solid it ensures good homogenization in the compound.
PEROXAN DC-P+ does not dissolve clearly in the resin system and is therefore not applicable for the production of cured parts when a high degree of transparency is required. For these applications, PEROXAN DC-P is recommended.
The stability of this Dialkyl peroxide in an UP resin is hardly influenced by the presence of metal accelerators, pigments or fillers.
Depending on working conditions, the following peroxide dosage level is recommended:
PEROXAN DC-P+: 1,0 to 2,0 phr
PEROXAN DC-P+ is recommended for the crosslinking of NBR, SBR, EP(D)M, LDPE and EVA. Rubber compounds containing PEROXAN DC-P+ combine good processing safety with a fair speed of cure.
Safe processing temperature (t2): 130°C
Typical crosslinking temperature (t90): 170°C
The safe processing temperature t2 is defined as the temperature, at which the scorch time is longer than 20 minutes. The typical crosslinking temperature t90 is defined as the temperature at which 90% of the crosslinks in the compound are formed within about 12 minutes.
Please refer to the material safety data sheet (MSDS) for information concerning safe storage, use and handling of PEROXAN DC-P +. This information should be thoroughly reviewed prior to acceptance of this product. The MSDS is available for downloading at www.pergan.com or through contacting Pergan directly.
|
Schlavenhorst 71 D-46395 Bocholt Germany |
Phone: +49 (0)2871 / 99 02-0 Fax: +49 (0)2871 / 99 02-50 www.pergan.com |
HPUPCL/003/1019 Page 2 of 2 |
Material Safety Data Sheets
Here you can download safety data sheets according to Regulation (EC) no. 1907/2006.
Safety Data Sheets are an important source of information on chemicals, such as identity of the product,
occurring hazards, transport, safe handling and measures for prevention in case of danger