PEROXAN BIC
Peroxyester / Polymerization / Curing / Crosslinking
tert-Butyl peroxyisopropylcarbonate
75%,
Solution in odorless white spirits
PEROXAN BIC is used for the (co)polymerization of styrene, acrylates and methacrylates.
TDS HP
PEROXAN BIC is used for the curing of unsaturated polyester resins.
TDS UP
« back
PEROXAN BIC
Molecular weight:
CAS No.:
176.2
2372-21-6
Appearance:
Peroxide assay:
Active oxygen assay:
Density at 20°C:
clear liquid
appx. 75%
appx. 6.81%
0.88 g/cm³
in chlorobenzene:
Maximum storage temperature (Ts max):
Minimum storage temperature (Ts min):
Storage stability as from date of delivery:
25°C
0°C
6 months
Keep packaging tightly closed in a well ventilated place at indicated storage temperature. Keep away from reducing agents e.g. amines, acids, alkalis, heavy metal compounds (e.g. accelerators, driers, metal soaps). Never weigh out in storage room.
Oxidizing agent. Decomposes violently under the influence of heat or by contact with reducing agent. Never mix with accelerators.
Organic Peroxides are more or less stable products but will decompose under the influence of heat. To minimize a loss of quality during storage, it is important that the recommended maximum storage temperature is not exceeded. If a minimum storage temperature is given, an undesirable process such as a solidification or phase separation, is known to occur below this temperature.
|
Flash point: SADT: |
50°C 60°C |
|
|
The SADT (Self Accelerating Decomposition Temperature) is the lowest temperature at which a self accelerating decomposition may occur.
|
Schlavenhorst 71 D-46395 Bocholt Germany |
Phone: +49 (0)2871 / 99 02-0 Fax: +49 (0)2871 / 99 02-50 www.pergan.com |
HPUPCL/003/0919 Page 1 of 2 |
PEROXAN BIC
Peroxyester / Polymerization / Curing / Crosslinking
Polymerization of styrene:
PEROXAN BIC may be used in polymerization and copolymarization of styrene.
In a mass process PEROXAN BIC can be used to increase polymerization rates.In suspension polymerization processes, PEROXAN BIC is often used for reduction of residual styrene content during the final polymerization stage. PEROXAN BIC is a benzene-free replacement of tert-Butyl peroxybenzoate (PEROXAN PB).
Temperature range: 95 to 125°C
Dosing: 0,02 to 0,1 phr
Polymerization of acrylates and methacrylates:
PEROXAN BIC can be used as initiator for the solution, bulk and suspension (co)polymerization of acrylates and methacrylates.
Temperature range (solution polym.): 100 to 170°C
Dosing: 0,1 to 1 phr
PEROXAN BIC is used for the curing of unsaturated polyester resins at high temperatures.
PEROXAN BIC is preferred for the curing of UP resin based hot press moulding formulations in the temperature range from 140° to 160°C.
PEROXAN BIC gives a long shelf life stability of the compound.
PEROXAN BIC - in comparison with PEROXAN PB, tert-Butyl peroxybenzoate, - can be caracterized as a faster and more efficient peroxide. This means a faster and more optimal cure with a lower residual monomer content of the moulded part.
The decomposition products of PEROXAN BIC are low volatile compounds, which make the peroxide very suitable for production of e.g. microwave cookware.
Depending on application and working conditions, the following peroxide and when applicable cobalt accelerator dosage levels are recommended:
PEROXAN BIC: 1,0 to 2,0 phr
Please refer to the material safety data sheet (MSDS) for information concerning safe storage, use and handling of PEROXAN BIC. This information should be thoroughly reviewed prior to acceptance of this product. The MSDS is available for downloading at www.pergan.com or through contacting Pergan directly.
|
Schlavenhorst 71 D-46395 Bocholt Germany |
Phone: +49 (0)2871 / 99 02-0 Fax: +49 (0)2871 / 99 02-50 www.pergan.com |
HPUPCL/003/0919 Page 2 of 2 |
Material Safety Data Sheets
Here you can download safety data sheets according to Regulation (EC) no. 1907/2006.
Safety Data Sheets are an important source of information on chemicals, such as identity of the product,
occurring hazards, transport, safe handling and measures for prevention in case of danger